C
cooz
Member
Full Member
- Messages
- 20
- Reaction score
- 0
HO for sure.......
I think you meant to say HO FO SHO
Hi,how can i make this case,is a mine friend,woman. I can use only stain? Which ingot? Thanks
Firstly thanks for all answers,i think i try to make a thin additional weener on a single tooth on MO without preparation,to see the result,the coverage. The final color B1 A1. Has anyone ever solved a similar case? Thanks
Sorry for my english
Al can you make an e-book with all your case photos, tips and presentations that you have been kind enough to share. I think alot of us would buy one.
You can link your face book pics to the site. I think that works, it might not if you have it private.
Al,
Normally when im working on a multi unit case with a mixtutre of underlying colours i tend to stick with the same opacity ingots to have a uniform opacity to work from. If i used a HO for the central implants then id also use a HO for at least the laterals also.
Mixing and matching opacaties would seem to be throwing more shade variables into the mix.Donno what u think on that?
Also ive only just started using the HO ingots as i never had access to HO with the CAD varient. Whats the thinnest these can go before they start loosing to much oppacity to be effective? .5 -.6?
thanks.
How do I do that. No its not private.
I think its around .6, I have the areas over the abutments .9. I used gold die spacer on 8 & 9 dies so Im going to reduce it slow and wet it to see how thin I dare to take them.
HOO is chaulk white and Im going to BL3, I dont want grey show through but I also dont want headlights.
A had a Dr I really respect suggest I make the centrals, (since they are so large and prominent),have a lower value and the lats have a higher value to take your attention away from the prominence of 8 & 9.
One lat is a full crown the other is a venner. HO on a veneer would be hideous. Thats why Im went with LT on both lats.
He also suggested I go with low value high croma on the cuspids.
So that would be low value centrals higher value on the lats and low value high croma on the cuspids back.
The challange is to get lower value on HO.