Yes via e-mail... I wait for answer I want stl file only for MATRIX (art code 6480 1037 )

Hi I want to found stl file for exocad to add attachment from HERAUS KUZLER anteriorlock and duoblock ( http://heraeus-kulzer.com/int2/int/dental_technician/products_a_to_z/hera_1/TAttachments.aspx#wr-tab-2 ) Thanks

Hi Dimitris What is the name of scanner ? I not find any useful info for this scanner in web. Where can find any info of this scanner and who is the dealer in Europe ? Thanks

Thanks Drizzt i will wait your comments for reveng scanner

Is That you have say for synergiascan and not for REVENG 3D from same company ? What about for reveng 3d hi level model Hi-level ?

Why ? Do you use it ? What is con ? What model standart, hi level , entry level ? Thanks

Hi to All I have trouble to deciding which scanner to buy. What is your opinion in this two models: 1. D scanning software, software scansioni 3D, scanner 3D, EGS Srl or 2. .:: smart optics 3D Scanner Activity 101 ::. I have small dental laboratory. If in future if I decide to buy...

it is problem with sort time dry time in opaquer . try to 10min minimum time in dry opaquer with thin layer of this

@AI In this case what glaze you use it ? Is it powder glaze or paste ? I use powder glaze mix with liquid. The final result is surface with many small tiny bubbles like pimples . These problem saw with loupe x3.5. Then i remove it with silicone rubber and diamande paste. What company (brand)...

I use VMK MASTER but i not like the color. e.g The color in 3L1.5 comes out as a dull green shade. I have tried Increased the vakoum increase the temperature to no avail. So I gave up. Do you have a solution ? I use Multimat furnace . Thanks

I do not want to sell. Is very good layering very smooth but in the same brand the poweder material is suck (in my opinion). So what I do is just paint the metal with this paste and stratified layering with another brand. But as stated by the problem and my question is if it is good in bonding...

I have many many stock of paste opaquer from other porcelain. My build is creation or GC. My question is whether doing good bond paste opaquer with build powder

Hi to all I have a question that puzzles me. Is it acceptable to use a opaker paste from X company and builds a porcelain from Y company? Is it possible to create a problem with this way? To mention one example on the above. OPAKER paste with ivoclar inline and build with Creation powder.

Hi I would like your opinion on this particular porcelain. Pulse MC from ceramay Color results, ease of stratification, some tricks etc I think to try it. I love the idea that it is lowfusing I've tried GG, creation, inline. All of them is good porcelain but i dont like the strong ...

so what I am trying to say is that the oven needs cleaning. In the new oven that have electric resistance in a glass does not make you put Purge All / Plus. All the dirt will burn at 1050 degrees Celsius for 10 minutes. This will solve her problem. The problem is due for multiple reasons...

your solution is : Start your furnace in glaze programm without anything in furnace. Change the end temp in 1050 celsius and hold time in 10min After that test result in one PFM case. If exist then repeat above. Thanks

sorry wrong post

Hi I dont undersand where put this temp. In oxidation, in 1 opaquer, in 2 opaquer ? Where ? Thanks

Hi I have the same furnace. You must replace in firing parameters in emax B=403 celcius with V1=450 celsius. dentin1 for emax for multimat: B=450=Low temp S=4.00min=drying time T^=40=heat rate T=750=high temp H=1min=holding time V1=450=vacumstart V2=749=vacum end

Hi Can you write the rgb or lab color of vita clasic shade quide ? Thanks