That's when they usually crack in these situations. They have several firings in there thermal history and the stress builds, then releases in that glaze firing.
Again, in these situations with thick-to-thin-to-thick geometries, add a long term cooling to at least the glaze cycle. If you can control by temperature, cool to 500C; if you control by time, 5-7 minutes will usually do it.