Forums
New posts
Search forums
What's new
New posts
Latest activity
Articles
Members
Current visitors
Log in
Register
What's new
Search
Search
Search titles only
New posts
Search forums
Menu
Log in
Register
Install the app
Install
Forums
Lab talk, the good, the bad, and the ugly
Metal
What finnishing stones are you using
JavaScript is disabled. For a better experience, please enable JavaScript in your browser before proceeding.
You are using an out of date browser. It may not display this or other websites correctly.
You should upgrade or use an
alternative browser
.
Reply to thread
Message
<blockquote data-quote="Wyolab" data-source="post: 19347" data-attributes="member: 1394"><p>I use Noritake EX-3, and Penceram 52-sf. I am thinking about switching to Penceram 40 though, I have been told it doesn't oxidize as dark. Noritake isn't very silver sensitive so don't worry about that, unless you have other systems that will react to being fired in the same furnace as alloys containing silver. Stones don't seem to cause a problem if that's how you like to finish your metal. I use a heatless mizzy to grind down the sprue, then I have used Blue Dolphin green stones, even shofu dura-white without problems. Any stones should be fine, just don't use the same stone on your NP alloys as yuor HN alloys. I do let them soak in distilled water in the ultrasonic for five minutes after metal finishing, then blast them with the steamer before degassing. Hope that helps.</p></blockquote><p></p>
[QUOTE="Wyolab, post: 19347, member: 1394"] I use Noritake EX-3, and Penceram 52-sf. I am thinking about switching to Penceram 40 though, I have been told it doesn't oxidize as dark. Noritake isn't very silver sensitive so don't worry about that, unless you have other systems that will react to being fired in the same furnace as alloys containing silver. Stones don't seem to cause a problem if that's how you like to finish your metal. I use a heatless mizzy to grind down the sprue, then I have used Blue Dolphin green stones, even shofu dura-white without problems. Any stones should be fine, just don't use the same stone on your NP alloys as yuor HN alloys. I do let them soak in distilled water in the ultrasonic for five minutes after metal finishing, then blast them with the steamer before degassing. Hope that helps. [/QUOTE]