Forums
New posts
Search forums
What's new
New posts
Latest activity
Articles
Members
Current visitors
Log in
Register
What's new
Search
Search
Search titles only
New posts
Search forums
Menu
Log in
Register
Install the app
Install
Forums
Lab talk, the good, the bad, and the ugly
Dental-CAM
removing Ti base
JavaScript is disabled. For a better experience, please enable JavaScript in your browser before proceeding.
You are using an out of date browser. It may not display this or other websites correctly.
You should upgrade or use an
alternative browser
.
Reply to thread
Message
<blockquote data-quote="Patrick Coon" data-source="post: 238955" data-attributes="member: 11366"><p>Not official, but seems to work well:</p><p></p><p>Base Temp: 400C / 752F</p><p>Dry Time: 6 minutes</p><p>Rate of Rise: 60C / 140F</p><p>High Temp: 600C / 1112F</p><p>Hold: 2 minutes</p><p>Vacuum On: 400C / 752F</p><p>Vacuum Off: 600C / 1112F</p><p></p><p>This works well, but I can't guarantee the TiBase won't be oxidized. If it doesn't just come apart, put in the Ultrasonic for 2 minutes, that will loosen the "dust" from the cement allow it to slip apart.</p></blockquote><p></p>
[QUOTE="Patrick Coon, post: 238955, member: 11366"] Not official, but seems to work well: Base Temp: 400C / 752F Dry Time: 6 minutes Rate of Rise: 60C / 140F High Temp: 600C / 1112F Hold: 2 minutes Vacuum On: 400C / 752F Vacuum Off: 600C / 1112F This works well, but I can't guarantee the TiBase won't be oxidized. If it doesn't just come apart, put in the Ultrasonic for 2 minutes, that will loosen the "dust" from the cement allow it to slip apart. [/QUOTE]