Forums
New posts
Search forums
What's new
New posts
Latest activity
Articles
Members
Current visitors
Log in
Register
What's new
Search
Search
Search titles only
New posts
Search forums
Menu
Log in
Register
Install the app
Install
Forums
Lab talk, the good, the bad, and the ugly
Dental-CAM
Quick Sintering Zolid FX Zirconia
JavaScript is disabled. For a better experience, please enable JavaScript in your browser before proceeding.
You are using an out of date browser. It may not display this or other websites correctly.
You should upgrade or use an
alternative browser
.
Reply to thread
Message
<blockquote data-quote="deadhead" data-source="post: 253350" data-attributes="member: 19095"><p>with the new multi-layer shaded pucks from AG(Zolid-FX Multi-layered) the Zirconia contains cubic ZR and thats why it fires at 1450 because since they added cubic ZR to their powder if you over heat your color will be off because you will be burning the cubic ZR. just spoke with an AG rep about this and thats what he said. they added cubic ZR to get the strength and a better "realistic" look so if you fire too high you will get the "dull/fake" look. we were using ZOLID FX with the pre-sinter liquids and now we use their multi-layer pre shaded pucks, but to achieve good shades we noticed you have to use 16mm or higher in puck thickness so you can move the units up or down depending on how much trans u want. AG is also coming out the pre-shaded pucks too, so then you wouldnt have to worry about placement since the puck will be same shade throughout. hope this infor is helpful. happy milling <img src="data:image/gif;base64,R0lGODlhAQABAIAAAAAAAP///yH5BAEAAAAALAAAAAABAAEAAAIBRAA7" class="smilie smilie--sprite smilie--sprite1" alt=":)" title="Smile :)" loading="lazy" data-shortname=":)" /></p></blockquote><p></p>
[QUOTE="deadhead, post: 253350, member: 19095"] with the new multi-layer shaded pucks from AG(Zolid-FX Multi-layered) the Zirconia contains cubic ZR and thats why it fires at 1450 because since they added cubic ZR to their powder if you over heat your color will be off because you will be burning the cubic ZR. just spoke with an AG rep about this and thats what he said. they added cubic ZR to get the strength and a better "realistic" look so if you fire too high you will get the "dull/fake" look. we were using ZOLID FX with the pre-sinter liquids and now we use their multi-layer pre shaded pucks, but to achieve good shades we noticed you have to use 16mm or higher in puck thickness so you can move the units up or down depending on how much trans u want. AG is also coming out the pre-shaded pucks too, so then you wouldnt have to worry about placement since the puck will be same shade throughout. hope this infor is helpful. happy milling :) [/QUOTE]