Forums
New posts
Search forums
What's new
New posts
Latest activity
Articles
Members
Current visitors
Log in
Register
What's new
Search
Search
Search titles only
New posts
Search forums
Menu
Log in
Register
Install the app
Install
Forums
Lab talk, the good, the bad, and the ugly
Zirconium
Katana STML/UTML shading issues
JavaScript is disabled. For a better experience, please enable JavaScript in your browser before proceeding.
You are using an out of date browser. It may not display this or other websites correctly.
You should upgrade or use an
alternative browser
.
Reply to thread
Message
<blockquote data-quote="SmartLabJon" data-source="post: 286663" data-attributes="member: 14947"><p>Hey all, I wanted to pick your collective brains!</p><p></p><p>My ceramists are complaining (and have for a while) about hitting shades with anterior zirconia. We are currently using Katana STML and some UTML. We have used Bruxzir Anterior in the past and they have had the same complaints. The complaints are all over the place like too orange, too dark, too grey, too white, you name it. I am waiting for a response back from Zahn but I wanted to see if any of you have issues with it. Is it a stain and glaze technique problem or is there something different I can do during design/nesting/milling to help them out? I've also had CMC mill some and it makes no difference they still complain. I don't do ceramics so I am trying to help them the best I can. We use a Wieland Select Hybrid (but dry mill only) and we have 2 Sintra Plus furnaces if that helps. </p><p></p><p>Thanks!</p></blockquote><p></p>
[QUOTE="SmartLabJon, post: 286663, member: 14947"] Hey all, I wanted to pick your collective brains! My ceramists are complaining (and have for a while) about hitting shades with anterior zirconia. We are currently using Katana STML and some UTML. We have used Bruxzir Anterior in the past and they have had the same complaints. The complaints are all over the place like too orange, too dark, too grey, too white, you name it. I am waiting for a response back from Zahn but I wanted to see if any of you have issues with it. Is it a stain and glaze technique problem or is there something different I can do during design/nesting/milling to help them out? I've also had CMC mill some and it makes no difference they still complain. I don't do ceramics so I am trying to help them the best I can. We use a Wieland Select Hybrid (but dry mill only) and we have 2 Sintra Plus furnaces if that helps. Thanks! [/QUOTE]