Forums
New posts
Search forums
What's new
New posts
Latest activity
Articles
Members
Current visitors
Log in
Register
What's new
Search
Search
Search titles only
New posts
Search forums
Menu
Log in
Register
Install the app
Install
Forums
Community discussion
Fixed
F.C. Gold Casting
JavaScript is disabled. For a better experience, please enable JavaScript in your browser before proceeding.
You are using an out of date browser. It may not display this or other websites correctly.
You should upgrade or use an
alternative browser
.
Reply to thread
Message
<blockquote data-quote="sixonice" data-source="post: 21148" data-attributes="member: 2"><p>in my opinion, your burnout temperature is too high for these full cast alloys, especially if the beauty cast is a low temperature investment (which I think it is??) if this is the case you should be burning out at 900-1000F. now if the beauty cast is a high heat investment, i would burn out to the manufacturers instructions, then 30 min prior to casting I would still turn down the temp to 950 or 1000F then cast. sounds like your mold is too hot.</p></blockquote><p></p>
[QUOTE="sixonice, post: 21148, member: 2"] in my opinion, your burnout temperature is too high for these full cast alloys, especially if the beauty cast is a low temperature investment (which I think it is??) if this is the case you should be burning out at 900-1000F. now if the beauty cast is a high heat investment, i would burn out to the manufacturers instructions, then 30 min prior to casting I would still turn down the temp to 950 or 1000F then cast. sounds like your mold is too hot. [/QUOTE]