Forums
New posts
Search forums
What's new
New posts
Latest activity
Articles
Members
Current visitors
Log in
Register
What's new
Search
Search
Search titles only
New posts
Search forums
Menu
Log in
Register
Install the app
Install
Forums
Lab talk, the good, the bad, and the ugly
Dental-CAM
Adding support bridges milling.
JavaScript is disabled. For a better experience, please enable JavaScript in your browser before proceeding.
You are using an out of date browser. It may not display this or other websites correctly.
You should upgrade or use an
alternative browser
.
Reply to thread
Message
<blockquote data-quote="Sevan P" data-source="post: 325273" data-attributes="member: 7766"><p>Low and slow will work like MarkPeters said or support just to be safe. Here are some examples of ones i have done in the past, all seated 100%. 3 to 4 lingual sprues at 3mm each sprue.</p><p>[ATTACH]36682[/ATTACH][ATTACH]36683[/ATTACH]</p><p></p><p>Then i set in the oven like so.</p><p>[ATTACH]36686[/ATTACH]</p><p></p><p>Then when you get jittered while coloring the bridge and drop and break the support bar off.</p><p>[ATTACH]36684[/ATTACH]</p><p></p><p>You add some more time to the already long cycle, usually 10hr heat and 5 hr cooldown make it 14hr heat 5 hr cool. It drops right in like a glove.</p><p>[ATTACH]36685[/ATTACH]</p><p></p><p>So what ever tickles your pickle, I say. Just do NOT over sprue the lingual that will also cause pulling and breaking while sintering. Keep it simple/ Facial you can add more then have the cam cut most but at least 3 off.</p></blockquote><p></p>
[QUOTE="Sevan P, post: 325273, member: 7766"] Low and slow will work like MarkPeters said or support just to be safe. Here are some examples of ones i have done in the past, all seated 100%. 3 to 4 lingual sprues at 3mm each sprue. [ATTACH]36682[/ATTACH][ATTACH]36683[/ATTACH] Then i set in the oven like so. [ATTACH]36686[/ATTACH] Then when you get jittered while coloring the bridge and drop and break the support bar off. [ATTACH]36684[/ATTACH] You add some more time to the already long cycle, usually 10hr heat and 5 hr cooldown make it 14hr heat 5 hr cool. It drops right in like a glove. [ATTACH]36685[/ATTACH] So what ever tickles your pickle, I say. Just do NOT over sprue the lingual that will also cause pulling and breaking while sintering. Keep it simple/ Facial you can add more then have the cam cut most but at least 3 off. [/QUOTE]