But hey this happened to me a while back and i said F it! and set my cycle to 12hrs to high temp, hold for 2.5 then internal cool down and fit fir like a glove!
So you can make the call, just bury it into the sintering beads acting as a pillow, i use the super small beads, large beads will not work the same.
I ran it without.. I put an extra 30 min. at high hold and doubled the cooling time. Fit was perfect. Bruxir 16 as this is all this Dr. wants. No beads. Programat 1600. When using the base do you sinter standing up up or lay flat ?
I ran it without.. I put an extra 30 min. at high hold and doubled the cooling time. Fit was perfect. Bruxir 16 as this is all this Dr. wants. No beads. Programat 1600. When using the base do you sinter standing up up or lay flat ?
If you have a support brace, vertically. like so.It's not the hold time that makes or breaks it, it is the climb time to high temp that can make the bridge(s) warp.