hi guy does anyone have 3shape and AG motion2? I already have AG material and import to 3shape but the file still need set something , not like the cad file from exocad especially the abutment, I need set the screw hole.... and sometimes will have issue

Did anyone have tried use other brand skin’s dongle To drive the oringinal exocad? Will it work? Or some worked some not? If anyone had tried AG will be best

Hi guys, Does anyone now using other CAM with Ceramill motion2? Thank you

Hi guys, I have a question , can i use the sintron strategy to mill zirconia? Because my AG motion2 milling too fast and I want it slow down If I do that , Will anything bad happened?

hi guys , does anyone know how to modify these xml file? My cam is exocam I have try to open it with xml editor , all aren't worked the reason I want do that is because I hope can change the tool 0.3 to 0.6

Hi guys I got a map 400 now I feel the margin part is not so real than 3shape D900L dose anyone know what's going on , or It's normal? I have check the scan quality is very high and done the correct calibration thank you

damn My boss buy a CADCAM system from AG and I seem a new cam called exocam... and very different with SUM3D does anyone know this cam? like modify tool ? strategies? thank you

Hi guys, I’m using vita M6000now I have a question, what is different with Zubler and dekema?and ivoclar P710? As I know P710 have heat sensor. But why others popular? And what should I adjust When I bake 8units bridge? Sppl said rate sppl said temperature sppl said holding time Why?

Hi guys, I wondering know what kind of practice you did every day? As I watch the jungo endo’s lecture , I did 2more morphologies every day But if I want practice more about other thing What kind of practice I should do?

Guys... I'm so confused I'm using vita vm9 sombody tell me my ceramics logic is wrong, He said the copping and framework should reduce the target color (like A3>A2) otherwise the value or color will wrong... I'm so confused now... can anyone share the ceramics logic? like is this right...

Hi guys, I wonder know Is all teeth have opalescence? If i see the green or grey or yellow shade at incisal area Is that means that is opalescence? or if it's not blue or violet , then this teeth doesn't have opalescence? the reason I ask is because VM9~15 only create 5 color effect opal

Hi guys, I wonder know , how do you learn Emax and ceramics in your country? In my country , we need learn from lab owner, Even this lab sucks... So how do you learn the ceramics of ever brand? Thanks

Hi guys I already have 350i, and now I want buy roland But reseller told me I need buy a new sum3d milling box And that cost 6k usd in my country ...

Hi guys, My scanner is D900L and milling machine is 350i the CAN Is sum3D I don't know why if abutment have heavy chamfer , chamfer or shoulder there will have a space in the chamfer part! I means margin is fit! but there are space after margin I can see the space with fit check and micro scope...

Hi guys I have a question How do I avoid this ?

Hi guys, I bought a book from Ubassy, And I notice I don't know so many basic thing!! I thinking about Is there a book I must buy and read? To let me know what is the basic? about color , about stain about ceramics Thanks for advice

Hi guys happy new year Does anyone have used 600MPa Zirconia? I use Metoxit smile , and I feel it's so hard to make margin more thiner But I hope I can find other brand looks like the EmaxLT and easy to grid the margin Thanks

Hi guys, When my dentist use the pick up coping impressions, I only can use GC patten resin to deal the abutment part Can you share that how do you do this type case? Thank you

Hi guys my dentist ask me why zirconia veneer will fail bond? He use the 3M Universal Any suggestions?

Hi all I'm so confused why vita give me a liner list But if I follow this list I can't get corrected color!!? If coping is A3 I use eL4/EL6 liner After dentine I will get A2!! Wtf!