I have but there is nothing in it to say how its done , looked all over the Internet and asked all my Tech friends, so im exasperated. Need help with this.
Thanks Patrick ,and i suppose HO would block out the underlying colour at 4mm .Think I will make a PFM and a HO and see which come out best .Dont have enough time for Zirconia unfortunately.
What Emax press ingot is best for ultra thin emax veneers. I want to just do shape corrections. Abd what is the min thickness that i can go with said emax material
Dentist to a technician: I can do this job with my eyes shut so stop telling me what to do !!!
Technician : Next time please open just one of your eyes slightly and we may get a better job!
Thats all i got to work with ,what would be a good offer for this stuff ?I dont know how full the porcelains are but the ingots seem on the low side !What would you guys offer
thanks
Hi there i was wondering what is the best way to work of the margin of a zirconia coping after it has been milled and sintered, im always left with a thin margin that i have to work off!
When i mill out of metal i have the same result a small collar around margin !
Is there a way to design it...
really looks good ,only critique i have is that you should have sectioned in between teeth better ! Would have looked more separate, but overall very impressive result for full zirconia !!