I expressed myself badly .. I did mean, if you use the so high to firing,, who knows if the temperature of the bake of glaze is higher in proportion ..;)
NO, I have not had problems.
But I like to be on the safe side and sleep soundly ..
And if it would increase the resistance to fracture, it would be even more peaceful
I get on well with emax
I wonder if anyone has had the same problem and how he solved it.
The ceram bond has become more dry and its texture is less creamy.
Resulting in difficulty in applying it.
With which the liquid can be diluted?
Opaque liquid, liquid glaze or what?
Have any of you tried with reliable results?
What brands of zirconia opaque puck can you recommend?
To mill copings on implant abutments, where you do not see in transparency the gray of the stump.
I have to recommend to a colleague of mine that I usually milling for me some copings, and that ended the opaque puck, and he tells me that...
Wanting to differentiate the variety and price of PFM, I will introduce a simple ceramic that gives excellent results using only 2 or 3 powders.
What are in your opinion the best with these features
This is biscuit,
I still have to change some form and characterize a little the shade .
Obviously the translucency is not optimal, but having 0.8 mm zirconia,
there remained no much room for layering ceramic.
Patrick, if I decide to try again to stratify with e.max, what color would you suggest to make the zirconia framework, knowing that I have to get a 3.5?