  1. N

    Air bubbles, heat cure

    so now my thoughts are that I need to use less monomer and wait a bit longer almost to a point where it's harder to put the dough inside the flask, also some of you mentioned that boiling water is bad, but the instruction says that this material is designed for fast heat curing and it says to...
  2. N

    Air bubbles, heat cure

    Instructions don't make sense, it says mix ratio is 10g of powder and 4ml of monomer..which is ridiculous, I tried that and only like 1/4 of polymer gets wet, because 4ml is not even close to enough lol, it also says that adding 5ml instead of 4ml will extend working time up to 2-3 hours, which...
  3. N

    Air bubbles, heat cure

    the thing with instructions is that there aren't any..I mean the product does not come with the instruction papers, the one sales rep gave me is just weird, I don't trust it, I tried if ofc, ratio was off, you couldn't even mix it.. I just doubt it's the real thing, I know few techs who use this...
  4. N

    Air bubbles, heat cure

    Hello, I'm having issues with PlastoDon N (Scheftner) heat cure material, whenever there's thicker parts of the denture (usually under molars) I get air bubbles, sometimes few, sometimes a lot, I'll show you pics when there's a lot of them, I use to use Meliodent, it was great, there was no...
  5. N

    Taking shades

    Hey, I don't know where to post this, but I am curious what is your shade taking protocol, so I'll leave few questions, please reply, it will help me (and maybe other too) a lot :) 1. What is your shade taking protocol? 2. What do yo use for taking shades? 3. Are you satisfied with your current...
  6. N

    Exocad virtual gingiva design problems

    thx, I'll try that
  7. N

    Exocad virtual gingiva design problems

    Hello, I'm trying to create a bridge construction on implants with virtual gingiva, now I have done this few times before, but I often run into the same problem and I have no idea why, it seems that if the construction is bigger - my chances of success are smaller lol, I looked for answers on...
  8. N

    AI in the dental world

    I'm a dental tech for over 10 years and speaking about prices all I can say is that we (well not really we, but more like generations before most of us became techs) f***ed ourselves, because right now we are probably in the worst situation since before the implants came around, because many of...
  9. N

    Exocad all on 4 pmma gingiva merge error

    Solved it, turns out I had to select in dentalDB anatomic waxup and pontic waxup instead of anatomic crown and anatomic pontic, so now it works fine, but tbh I still don't see any sense in that, I mean why would it matter..but turns out it does
  10. N

    Exocad all on 4 pmma gingiva merge error

    Maybe you will spot what am I doing wrong easily..because I have no clue
  11. N

    Exocad all on 4 pmma gingiva merge error

    So far no luck.. 1. Cut some room under teeth - you mean the space between rean gingiva and anatomic teeth? Because I have done that, there is space 2. Also done that, teeth are smooth 3. What do you mean exactly? Virtual gingiva is not very thick, I don't need much gingiva, so it probably is...
  12. N

    Exocad all on 4 pmma gingiva merge error

    Hello, this is first time I'm making pmma all on 4 with gingiva and I got this weird error, searched it on google, some guy had the same problem, but there was no solution (pictures I uploaded are his, not mine). it says "missing: error merging virtual gingiva" also just like in the picture it...
  13. N

    denture making equipment

    Hey everyone, I was thinking maybe I should upgrade my denture making setup, right now it's very simple, I use hand press, small electric stove (two holes) and two pots (wash, cure). I'm looking into hydraulic press and curing units, what are you guys using? Feel free to recommend something or...
  14. N

    Rayshape 3d printer

    Hello everyone, looking for my first printer, never used any printer before, since it'd be my first one - I'm not looking for anything big, got an offer from Rayshape: Professional DLP 3D Printer RAYSHAPE Shape 1 + - €7500 RAYSHAPE Full Solution Shape 1 +, ShapeCure, ShapeWash020s, 4kg of...
  15. N

    Which acrylic material are you using for dentures?

    Hello everyone, need your help, I've been using Meliodent (Kulzer) acrylics material for about 10 years, but it was discontinued and now you can't get it anywhere (at least in my country - Lithuania),so I need to find some other material, so far I found out that dental suppliers in my country...
  16. N

    noritake group

    I've been using white dental direkt zr for frameworks, what do you mean by "best to work with", to me they are all the same more or less, but I'm using only white zr, maybe there would be a difference with precolored zr, also I have no idea would it affect the color, meaning if I use the same...
  17. N

    noritake group

    hello. just started using noritake czr, I have lots of questions, let's start: 1. is there an adhesive for zr framework? 2. why is there 8 firing programs (I'm used to 1st, 2nd bake and glaze)? 3. how many bakes do you do usualy and which powders do you use in which bake? 4. do you use...
  18. N

    Heraeus Kulzer Heraceram

    started using 750, I think it looks better than heraceram for pfms, but the colors are different, if I need to do a3 on a white zr framework, I have to mix everything for a2, because it ends up being one shade darker, also it sometimes ends up having these transitions, but it may be my fault...
  19. N

    Dust collector

    Hey everyone, what kind of dust collectors do you guys use? I have 7 work tables, so all 7 need some kind of air extraction system, right now there are 4 people in the lab working everyday, 3 tables are empty, so I use industrial vacuum cleaner for each table (einhell 1930sa or something like...
  20. N

    pink opaque

    thx everyone, I was talking about this, finally found it, it's called Conalor (made by SpofaDental),posting this for the people who might search it in the future